TY - JOUR
T1 - Application of the Small Punch Creep test to predict times to rupture on magnesium alloys
AU - Andrés, D.
AU - Lorenzo, M.
AU - Lacalle, R.
AU - Álvarez, J. A.
AU - Alegre, J. M.
N1 - Publisher Copyright:
© 2016 Elsevier Ltd
PY - 2016/12/1
Y1 - 2016/12/1
N2 - The Small Punch Creep (SPC) test, first introduced by Parker in 1993, has been in continuous development ever since. Currently, it has a widespread utilization in the nuclear and aerospace industry, being mainly applied to steel characterisation. Thanks to its potential, especially for the reduced size of the samples and shorter testing times than the conventional tests, its application in light alloys has been proposed. The use of light alloys in several sectors is growing continuously, since they contribute to reduce the weight of components. In this work, the behaviour of the magnesium alloy AZ31 has been analysed at temperatures between 398 K and 523 K. A relationship between conventional and SPC tests has been established, by comparing time to rupture, as well as the Larson-Miller (LM) and Orr-Sherby-Dorn (OSD) parameters. On the other hand, the LM and OSD parameters have been obtained from the results of the SPC tests (turned into their equivalent uniaxial values) and they have been compared to the ones derived from the conventional tests, confirming the potential of this testing technique and its accuracy for the extrapolation of times to rupture in creep conditions.
AB - The Small Punch Creep (SPC) test, first introduced by Parker in 1993, has been in continuous development ever since. Currently, it has a widespread utilization in the nuclear and aerospace industry, being mainly applied to steel characterisation. Thanks to its potential, especially for the reduced size of the samples and shorter testing times than the conventional tests, its application in light alloys has been proposed. The use of light alloys in several sectors is growing continuously, since they contribute to reduce the weight of components. In this work, the behaviour of the magnesium alloy AZ31 has been analysed at temperatures between 398 K and 523 K. A relationship between conventional and SPC tests has been established, by comparing time to rupture, as well as the Larson-Miller (LM) and Orr-Sherby-Dorn (OSD) parameters. On the other hand, the LM and OSD parameters have been obtained from the results of the SPC tests (turned into their equivalent uniaxial values) and they have been compared to the ones derived from the conventional tests, confirming the potential of this testing technique and its accuracy for the extrapolation of times to rupture in creep conditions.
KW - Extrapolation techniques
KW - Magnesium alloys
KW - Small Punch Creep
UR - https://www.scopus.com/pages/publications/84995488361
U2 - 10.1016/j.tafmec.2016.08.004
DO - 10.1016/j.tafmec.2016.08.004
M3 - Article
AN - SCOPUS:84995488361
SN - 0167-8442
VL - 86
SP - 45
EP - 50
JO - Theoretical and Applied Fracture Mechanics
JF - Theoretical and Applied Fracture Mechanics
ER -