Compound Formation and Microstructure of As-Cast High Entropy Aluminums

Jon Mikel Sanchez; Iban Vicario; Joseba Albizuri; Teresa Guraya; Natalia Koval; Jose Garcia

doi:10.3390/met8030167

Compound Formation and Microstructure of As-Cast High Entropy Aluminums

Jon Mikel Sanchez
, Iban Vicario
, Joseba Albizuri
, Teresa Guraya
, Natalia Koval
, Jose Garcia

CSIC UPV Centro de Fisica de Materials CFM

Producción científica: Contribución a una revista › Artículo › revisión exhaustiva

30 Citas (Scopus)

5 Descargas (Pure)

Resumen

The aim of this work is to study the microstructure of four high entropy alloys (HEAs) produced by large scale vacuum die casting. Al40Cu15Mn5Ni5Si20Zn15, Al45Cu15Mn5Fe5Si5Ti5Zn20, Al35Cu5Fe5Mn5Si30V10Zr10, and Al50Ca5Cu5Ni10Si20Ti10 alloys formed a mixture of different structures, containing intermetallic compound (IC) and solid solution (SS) phases. The phases observed in the casting alloys were compared with the equilibrium phases predicted by Thermo-Calc. The measured densities varied from 3.33 g/cm−3 to 5.07 g/cm−3 and microhardness from 437 Hv to 887 Hv. Thus, the microhardness and estimated strength/density ratios are significantly higher than other lightweight high entropy alloys (LWHEAs).

Idioma original	Inglés
Número de artículo	167
Publicación	Metals
Volumen	8
N.º	3
DOI	https://doi.org/10.3390/met8030167
Estado	Publicada - 9 mar 2018

Palabras clave

Lightweight high entropy alloys
Complex concentrated alloys
Microstructure
Intermetallic compounds
Thermo-Calc

Project and Funding Information

Funding Info
This work has been partially funded by the Basque Government through the project Elkartek:_x000D_ KK-2017/00007.

Acceder al documento

10.3390/met8030167

Metals-08-00167Versión publicada final, 3,9 MB

Otros archivos y enlaces

Enlace a la publicación en Scopus

Citar esto

@article{39c4d9e0ff0443aca92ea274d461c834,

title = "Compound Formation and Microstructure of As-Cast High Entropy Aluminums",

abstract = "The aim of this work is to study the microstructure of four high entropy alloys (HEAs) produced by large scale vacuum die casting. Al40Cu15Mn5Ni5Si20Zn15, Al45Cu15Mn5Fe5Si5Ti5Zn20, Al35Cu5Fe5Mn5Si30V10Zr10, and Al50Ca5Cu5Ni10Si20Ti10 alloys formed a mixture of different structures, containing intermetallic compound (IC) and solid solution (SS) phases. The phases observed in the casting alloys were compared with the equilibrium phases predicted by Thermo-Calc. The measured densities varied from 3.33 g/cm−3 to 5.07 g/cm−3 and microhardness from 437 Hv to 887 Hv. Thus, the microhardness and estimated strength/density ratios are significantly higher than other lightweight high entropy alloys (LWHEAs).",

keywords = "Lightweight high entropy alloys, Complex concentrated alloys, Microstructure, Intermetallic compounds, Thermo-Calc, Lightweight high entropy alloys, Complex concentrated alloys, Microstructure, Intermetallic compounds, Thermo-Calc",

author = "Sanchez, \{Jon Mikel\} and Iban Vicario and Joseba Albizuri and Teresa Guraya and Natalia Koval and Jose Garcia",

note = "Publisher Copyright: {\textcopyright} 2018 by the authors. Licensee MDPI, Basel, Switzerland.",

year = "2018",

month = mar,

day = "9",

doi = "10.3390/met8030167",

language = "English",

volume = "8",

journal = "Metals",

issn = "2075-4701",

publisher = "Multidisciplinary Digital Publishing Institute (MDPI)",

number = "3",

}

TY - JOUR

T1 - Compound Formation and Microstructure of As-Cast High Entropy Aluminums

AU - Sanchez, Jon Mikel

AU - Vicario, Iban

AU - Albizuri, Joseba

AU - Guraya, Teresa

AU - Koval, Natalia

AU - Garcia, Jose

PY - 2018/3/9

Y1 - 2018/3/9

N2 - The aim of this work is to study the microstructure of four high entropy alloys (HEAs) produced by large scale vacuum die casting. Al40Cu15Mn5Ni5Si20Zn15, Al45Cu15Mn5Fe5Si5Ti5Zn20, Al35Cu5Fe5Mn5Si30V10Zr10, and Al50Ca5Cu5Ni10Si20Ti10 alloys formed a mixture of different structures, containing intermetallic compound (IC) and solid solution (SS) phases. The phases observed in the casting alloys were compared with the equilibrium phases predicted by Thermo-Calc. The measured densities varied from 3.33 g/cm−3 to 5.07 g/cm−3 and microhardness from 437 Hv to 887 Hv. Thus, the microhardness and estimated strength/density ratios are significantly higher than other lightweight high entropy alloys (LWHEAs).

AB - The aim of this work is to study the microstructure of four high entropy alloys (HEAs) produced by large scale vacuum die casting. Al40Cu15Mn5Ni5Si20Zn15, Al45Cu15Mn5Fe5Si5Ti5Zn20, Al35Cu5Fe5Mn5Si30V10Zr10, and Al50Ca5Cu5Ni10Si20Ti10 alloys formed a mixture of different structures, containing intermetallic compound (IC) and solid solution (SS) phases. The phases observed in the casting alloys were compared with the equilibrium phases predicted by Thermo-Calc. The measured densities varied from 3.33 g/cm−3 to 5.07 g/cm−3 and microhardness from 437 Hv to 887 Hv. Thus, the microhardness and estimated strength/density ratios are significantly higher than other lightweight high entropy alloys (LWHEAs).

KW - Lightweight high entropy alloys

KW - Complex concentrated alloys

KW - Microstructure

KW - Intermetallic compounds

KW - Thermo-Calc

KW - Lightweight high entropy alloys

KW - Complex concentrated alloys

KW - Microstructure

KW - Intermetallic compounds

KW - Thermo-Calc

UR - https://www.scopus.com/pages/publications/85044258687

U2 - 10.3390/met8030167

DO - 10.3390/met8030167

M3 - Article

SN - 2075-4701

VL - 8

JO - Metals

JF - Metals

IS - 3

M1 - 167

ER -

Compound Formation and Microstructure of As-Cast High Entropy Aluminums

Resumen

Palabras clave

Project and Funding Information

Acceder al documento

Otros archivos y enlaces

Huella

Citar esto