Electron beam welded high thickness Ti6Al4V plates using filler metal of similar and different composition to the base plate

J. L. Barreda*, F. Santamaría, X. Azpiroz, A. M. Irisarri, J. M. Varona

*Autor correspondiente de este trabajo

Producción científica: Contribución a una revistaArtículorevisión exhaustiva

132 Citas (Scopus)

Resumen

Compositional changes of the welds carried out by the electron beam welding process have been investigated in the present work. Addition of a filler metal in the weld fusion zone has been used to solve some problems by improving the behaviour of the joint by minimising either the porosity, the notching or the cracking susceptibility of the joint (Sanderson et al., Met. Constr. Br. Weld. J. (1972); Atsuta et al. 3er CISFFEL, Lion, Francia, September 1983; Nazarenko and Kaidalov, Technological procedures of electron beam welding and repair; Murphy and Turner, Weld. J. (1976)). Filler metal can also be used to weld high thickness plates by low-power electron beam welders (Ruge and Oestmann et al., Decker. Electron and Laser Beam Welding, 11W, 1976). The main purpose of this work is to investigate the behaviour of a 17 mm Ti6Al4V weld by the electron beam welding process with a filler metal of similar and dissimilar composition to the base plate. In the present work the initial results of 17 mm thickness Ti6Al4V plates welded with a 3kWEB welder and a filler metal of titanium alloy of the same and different composition to the base metal are presented.

Idioma originalInglés
Páginas (desde-hasta)143-150
Número de páginas8
PublicaciónVacuum
Volumen62
N.º2-3
DOI
EstadoPublicada - 15 jun 2001

Huella

Profundice en los temas de investigación de 'Electron beam welded high thickness Ti6Al4V plates using filler metal of similar and different composition to the base plate'. En conjunto forman una huella única.

Citar esto